Hydration behavior and formation of strätlingite compound (C2ASH8) in a bio-cement based on tri-calcium silicate and mono-calcium aluminate for dental applications: influence of curing medium

Hydration behavior and formation of strätlingite compound (C2ASH8) in a bio-cement based on tri-calcium silicate and mono-calcium aluminate for dental applications: influence of curing medium

Evaluation of the final setting time was carried out on the material pastes of normal consistency prepared with distilled water at a liquid/solid ratio of 0.23 ml/g as given in “Setting time” section. The recorded average setting time was 20 min at 37 °C (average of five readings). Figure 3 shows th...

Mô tả chi tiết

Lưu vào:

Hiển thị chi tiết
Tác giả chính:	Radwan, M. M.
Đồng tác giả:	Nagi, Shaymaa M.
Định dạng:	BB
Ngôn ngữ:	en_US
Thông tin xuất bản:	2023
Chủ đề:	Tri-calcium silicate Mono-calcium aluminate Calcium silicate Hydrate Strätlingite Cytotoxicity
Truy cập trực tuyến:	http://tailieuso.tlu.edu.vn/handle/DHTL/12858
Từ khóa:	Thêm từ khóa bạn đọc Không có từ khóa, Hãy là người đầu tiên gắn từ khóa cho biểu ghi này!

Tài liệu tương tự

Synthesis of calcium silicate hydrate (csh) from vietnam rice hush
Thông tin tác giả:: Pham Trung Kien, Phan Viet Hoang, Huynh Dai Phu

Interactions between calcium silicate hydrate (C-S-H) and calcium chloride, bromide and nitrate / Gilles Plusquellec, André Nonat
Thông tin tác giả:: Plusquellec, Gilles, và những người khác

Hydration of water- and alkali-activated white Portland cement pastes and blends with low-calcium pulverized fuel ash / I.G. Richardson...[et al.]
Thông tin tác giả:: Girão, A.V., và những người khác

Hydration behavior of an experimental tricalcium silicate/tetracalcium phosphate bio-cement in Streptococcus thermophiles bacterial solution in comparison with distilled water used as a root canal furcation perforation repair material
Thông tin tác giả:: Radwan, M. M.
Thông tin xuất bản: (2023)

Inﬂuence of the reactivity of the amorphous part of mechanically activated alite on its hydration kinetics / S.T. Bergold, F. Goetz-Neunhoeffer, J. Neubauer
Thông tin tác giả:: Bergold, S.T., và những người khác

In situ1H-TD-NMR: Quantiﬁcation and microstructure development during the early hydration of alite and OPC / Dominique Ectors... [et al.]
Thông tin tác giả:: Dietrich, Ulf, và những người khác

Confocal Raman microscopy as a non-destructive tool to study microstructure of hydrating cementitious materials / J. Higl, M. Köhler, M. Lindén
Thông tin tác giả:: Higl, J., và những người khác

Densiﬁcation of C-S-H is mainly driven by available precipitation space, as quantiﬁed through an analytical cement hydration model based on NMR data / Markus Königsberger, Christian Hellmich, Bernhard Pichler
Thông tin tác giả:: Markus Königsberger, và những người khác

Effects of temperature on the atomic structure of synthetic calcium–silicate–deuterate gels: A neutron pair distribution function investigation / Claire E. White
Thông tin tác giả:: White, Claire E.

Calcium silicate hydrate (C-S-H) gel solubility data and a discrete solid phase model at 25 °C based on two binary non-ideal solid solutions / Colin S. Walker...[et al.]
Thông tin tác giả:: Mihara, Morihiro, và những người khác

Performance of carbonated calcium silicate based cement pastes and mortars exposed to NaCl and MgCl 2 deicing salt
Thông tin tác giả:: Farnam,Yaghoob

Leaching behaviour of low Ca:Si ratio CaO–SiO 2 –H2O systems / S.W. Swanton, T.G. Heath, A. Clacher
Thông tin tác giả:: Swanton, S.W., và những người khác

Inﬂuence of crystallinity and surface area on the hydration kinetics of CA 2 / F. Hueller...[et al.]
Thông tin tác giả:: Goetz-Neunhoeffer, F., và những người khác

Micromechanical multiscale fracture model for compressive strength of blended cement pastes / Michal Hlobil, Vít Šmilauer, Gilles Chanvillard
Thông tin tác giả:: Hlobil, Michal, và những người khác

Phase evolution of C-(N)-A-S-H/N-A-S-H gel blends investigated via alkali-activation of synthetic calcium aluminosilicate precursors / Brant Walkley...[et al.]
Thông tin tác giả:: Nicolas, Rackel San, và những người khác

Comparing the pozzolanic behavior of sugar cane bagasse ash to amorphous and crystalline SiO2
Thông tin tác giả:: Soare,Marcela M.N.S. de s, và những người khác

Corrosion behaviour of steel in CAC-mixed concrete containing different concentrations of chloride
Thông tin tác giả:: Jin,Sung Ho

Production and hydration of calcium sulfoaluminate-belite cements derived from aluminium anodising sludge
Thông tin tác giả:: Costa,Eugênio Bastos da

NMR relaxation of molecules conﬁned inside the cement paste pores under partially saturated conditions / Andrea Bede, Alexandra Scurtu, Ioan Ardelean
Thông tin tác giả:: Bede, Andrea, và những người khác

Phân tích cấu trúc và tính chất quang của thủy tinh Calcium Fluororoborate và Calcium Fluororoborate Sulphate pha tạp dysprosium Structural analysis and optical properties of dysprosium-doped Calcium Fluororoborate and Calcium Fluororoborate Sulphate glas
Thông tin tác giả:: Trần Ngọc
Thông tin xuất bản: (2023)

Innovative approach to simulating the biodeterioration of industrial cementitious products in sewer environment. Part II: Validation on CAC and BFSC linings / Matthieu Peyre Lavigne
Thông tin tác giả:: Auer, Lucas, và những người khác

Stabilization of Recycled Demolition Aggregates by Geopolymers comprising Calcium Carbide Residue, Fly Ash and Slag precursors
Thông tin tác giả:: Arulrajah,Arul

In-situ and continuous monitoring of pore evolution of calcium sulfoaluminate cement at early age by electrical impedance measurement
Thông tin tác giả:: Tang,S.W.

Calcium aluminate based cement for concrete to be used as hermal energy storage in solar thermal electricity plants / M.C. Alonso... [et al.]
Thông tin tác giả:: Alonso, M.C., và những người khác

Tutorials in mathematical biosciences. II, Mathematical modeling of calcium dynamics and signal transduction / James Sneyd (Ed.) ; with contributions by R. Bertram ... [et al.].
Thông tin tác giả:: Bertram, R., và những người khác

Ameliorative effect of foliar application of calcium on vegetative growth and mineral contents of olive trees Kalmata and Manzanillo cultivars irrigated with saline water
Thông tin tác giả:: Hagagg, Laila F.
Thông tin xuất bản: (2021)

HIỆU QUẢ TẠO NGÀ SỬA CHỮA CỦA XI MĂNG CALCIUM SILICATE (BIODENTINETM) TRONG ỨNG DỤNG CHE TUỶ GIÁN TIẾP
Thông tin tác giả:: Trần Xuân Vĩnh
Thông tin xuất bản: (2023)

Evaluation of stem cell differentiation medicated with calcium phosphate nanoparticles in chlorohexidine paste
Thông tin tác giả:: Mahran, Abeer Hashem
Thông tin xuất bản: (2023)

Enhancement of waste activated sludge dewaterability using calcium peroxide pre-oxidation and chemical re-ﬂocculation
Thông tin tác giả:: Chen,Zhan

Chloride-induced corrosion of reinforcement in low-calcium ﬂy ash-based geopolymer concrete / M. Babaee, A. Castel
Thông tin tác giả:: M. Babaee, và những người khác

ẢNH HƯỞNG CỦA PROHEXADIONE-CALCIUM LÊN SỰ GIẢM ĐỔ NGÃ CỦA GIỐNG LÚA ST1 Ở CÁC MỨC BÓN PHÂN ĐẠM KHÁC NHAU
Thông tin tác giả:: Nguyễn, Minh Chơn
Thông tin xuất bản: (2023)

Influence of foliar spray with some calcium sources on flowering, fruit set, yield and fruit quality of olive Kalmata and Manzanillo cultivars under salt stress
Thông tin tác giả:: El-Hady, Eman S.
Thông tin xuất bản: (2023)

Physico-chemical interaction between mineral admixtures and OPC–calcium sulfoaluminate (CSA) cements and its inﬂuence on early-age expansion / Piyush Chaunsali, Paramita Mondal
Thông tin tác giả:: Chaunsali, Piyush, và những người khác

Impacts of hexitols on the hydration of a tricalcium aluminate-calcium sulfate mixture / Camille Nalet, André Nonat
Thông tin tác giả:: Nalet, Camille, và những người khác

Elemental and morphological analysis of enamel following the application of two bleaching systems with amorphous calcium phosphate: effect on enamel erosion susceptibility
Thông tin tác giả:: Nagi, Shaymaa M.
Thông tin xuất bản: (2023)

Characterization of a more sustainable cement produced with recycled drywall and plasterboards as set retarders
Thông tin tác giả:: Medina,Nelson Flores

Ảnh hưởng của một số dưỡng chất đa-vi lượng và số lần xử lý trước thu hoạch lên chất lượng và hiện tượng khô đầu múi trái quýt Hồng (Citrus reticulata Blanco) :
Thông tin tác giả:: Nguyễn, Trần Anh Huấn

ĐÁNH GIÁ CẢMGIÁC ĐAU VÀ NHẠYCẢM SAU ĐIỀU TRỊCHE TỦYTRỰC TIẾPVỚI VẬT LIỆU SINH HỌC CALCIUM SILICATE
Thông tin tác giả:: Bùi Huỳnh Anh
Thông tin xuất bản: (2023)

Utilisation of steel furnace slag coarse aggregate in a low calcium ﬂy ash geopolymer concrete / M.S.H. Khan...[et al.]
Thông tin tác giả:: Foster, Stephen J., và những người khác

Properties of magnesium silicate hydrates (M-S-H) / Dominik Nied
Thông tin tác giả:: Skibsted, Jørgen, và những người khác